New! Epoxy Sealer coatings for Wood/GRP/ Steel Clear epoxy coating performing excellent adhesion and flexibility for long term resistance. Used in osmosis treatment in GRP boats and as a anticorrosive primer for bare steel. Used for gluing wood and also for waterproofing primer for bare wood. MIXING RATIO A+B: 1 parts Sol.A + 1 part Sol.B by volume POT LIFE: 4-6 hours (20°C) - COLOUR: Clear BRUSH/ROLLER/SPRAY: READY FOR USE Max 5% Thinner 765 RECOATING: mini 6 hours max 24 hours T.COVERAGE: 12-14 m2./Lt
|
 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Skippers Polifiber Primer
Two component fibreglass primer
Special two-component primer developed to confer outstanding adhesion on fibreglass. It is applied as a primer coat on topsides, superstructures and bottom fibreglass surfaces. It can be applied direct onto gelcoat provided that a suitble surface degreasing and slight sanding with fine abrasive paper is being carried out before its application.
MIXING RATIO A+B: 10 parts Sol. A + 3 Sol. B by volume
POT LIFE: 4-6 hours; COLOUR: White
APPLICATION: Brush, Roller, Spray
DILUTION: brush, roller, spray: 15-30% Thinner 203 or F.Thinner 205; spray:25-35% Thinne 203
DRYING TIMES: touch dry: 2-3 hours; recoat time: 18-24 hours
TH.COVERAGE: 10 m2/Lt for 50 dry microns
|
|
|
|
|
|
|
|
Two component white polyurethane undercoat
Two-component polyurethane undercoat for boats and car body coating with excellent coverage and good filling power. Used as an intercoat on wood, steel or fibreglass surfaces or as a pre-treatment primer before overcoating with two-pack enamels (e.g. Acriglass, Space Top or Whitext).
MIXING RATIO A+B: 5 parts of Sol.A + 2 Sol.B by volume
POT LIFE A+B: 6-8 hours
COLOUR: white
APPLICATION: Brush, Roller, Spray
DILUTION: brush, roller:15-30% F.Thinner 205; spray:25-35% Thinner 203
DRYING TIMES: touch dry: 3-4 hours: recoat time: 12-24 hours
TH.COVERAGE: 14-15 m2/Lt for 35-40 dry microns
|
|
|
|
|
|
|
|
Two component epoxy coating
Satin epoxy paint for steel, aluminium, light alloys, fibreglass, cement and wood surfaces. Recommended as a primer or undercoat in the marine industry but also widely applied on floors, tanks and industrial plants containing or in contact with oils,naphta,kerosene and soda solutions as well as for the internal coating of potable water, performing a non toxic resistant film. Used as a primer can be overcoated with chlorinated, acrilyc or polyurethane coatings, providing strong adhesion base and long effective anticorrosive barrier. Certified by the Italian Health Authority for contact with drinking water.
MIXING RATIO A+B: 9 parts Sol.A + 1 Sol.B by volume or 100 parts Sol.A + 8 Sol.B by weight
POT LIFE A+B: 6-8 hours
COLOUR: white, grey, oxide red
APPLICATION: Brush, Roller, Spray
DILUTION: brush, roller: 10-15% Thinner 765; spray:15-25% Thinner 765
DRYING TIMES: touch dry: 2 hours; recoat time: 12-24 hours
TH.COVERAGE: 8-9 m2/Lt or 5-6 m2/Kg for 50 dry microns
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Epofond AM/90 Water based epoxy
High performance water based epoxy coating, provides anticorrosive protection on steel and outstanding characteristics on other substrates for typical applications. Epofond compared to other water based epoxies, has a longer pot life, which allows applications of up to 4 hours at 20°C. The product is generally ready for use, with the need to add only a very small percentage of water. This product has resistance to fuels, mineral oils, detergents, solvents. Used as a waterproof finish for internal boat part and freezing cells, tanks, insulating panels, wood etc, easy to clean. Ready for use Longer pot life Fast drying Easy sandpapering Product details: Mixing Ratio A+B : 100 parts A with 22 parts B by volume or (100:16 by weight) Application Method : Brush, Roller, Spray Thinning % : Brush-Spray : Ready for use or max 5% of water Roller : For touch ups only Recommended Thickness : 50-60 dry microns Theoretical Coverage : 7-8 m2 per Litres or 5-6 m2 per kg Colours : Grey Packaging Size A+B: 730ml, 2.75 L, 29kg
|
|
|
|
|
High-build two-component epoxy primer with anti-osmosis properties
High-build epoxy satin coating for all types of surfaces. The advantage to build up a thickness of 100-150 dry microns per coat allows sensible reduction of labour costs. Overcoatable with chlorinated rubber, epoxy or polyurethane coatings for high quality long lasting anticorrosive coating systems. Excellent as anti-osmosis pre-treatment on fibreglass boats. Provides outstanding chemical resistance in the marine environment, both in atmosphere or immersion conditions.
MIXING RATIO A+B: 85 parts Sol.A + 15 Sol.B by volume or 95 parts Sol.A + 5 Sol.B in by weight
POT LIFE A+B: 4- 6 hours at 20°C
COLOUR: Grey
APPLICATION: Brush, Roller (touch ups))
DILUTION: brush, roller: 10-15% Thinner 765, spray:25-35% Thinenr 765
DRYING TIMES: touch dry: 30 minutes; recoat time: 12 hours
TH.COVERAGE: 13 m2/Lt or 4-5 m2/Kg for 40 dry microns
|
|
|
|
|
Skippers Amtar Black-tar Epoxy Primer
Two component epoxy tar primer
High solids epoxy coating modified with special bituminous material. It can be applied at 100-120 microns per coat performing a black, tough gloss film with good adhesion to the substrate.Resistant to complete immersion. to sea and fresh water, crude oil, basic and acid solutions. Suggested as a primer for the protection of boat bottoms and structures immersed in the water.
POT LIFE A+B: 6-8 hours at 20°C
APPLICATION: Brush, Roller, Spray
DILUTION: brush, roller: 5-15% Thinner 765; spray: 15-30% Thinner 765
DRYING TIMES: touch dry: 4-6 hours; recoat time: 6-12 hours (do not exceed 16 hours)
TH.COVERAGE: 7 m2/Lt or 5m2/Kg for 100 dry microns
|
|
|
|
|
Waterproofing, anti-osmosis two component primer
Two-component epoxy coating performing excellent adhesion, waterproofing and mechanical characteristics such as flexibility and long term resistance. It may even glue surfaces which are not perfectly dry. Used for anti-osmosis treatment in fibreglass boat bottom. EPOSEALER 97 can be applied both on an appearently sound gelcoat or after that the faulty gelcoat has been removed completely. Also applied as anticorrosive primer for metal (cast iron and light alloys parts etc.). It is also used for gluing purposes (e.g. wood to wood, wood to fibreglass etc.). Used also for restoring old wooden boats, EPOSEALER 97 is absorbed by the grains in the wood conferring adequate waterproofing and mechanical resistance; for repairing purposes when used in combination with fibre sheets etc.
MIXING RATIO A+B: 2 parts Sol. A with 1 part Sol. B
POT LIFE A+B: 2-3 hours
COLOUR: Clear
APPLICATION: Stiff bristle brush
DILUTION: 5% Thinner 765 (30-40% Thinner 765 if used as a keying priemr)
DRYING TIMES: dust dry: 4-6 hours; recoat time: 18-24 hours
TH.COVERAGE: 5 m2/Lt for 100 dry microns
|
|
|
|
|